Charpy impact test

The Charpy impact test, also known impact test as the Charpy V-notch test, is a standardized high strain-rate test which determines the amount of energy absorbed by a material during fracture. This absorbed energy is a measure of a given material's notch toughness and acts as a tool to study temperature-dependent ductile-brittle transition. It is widely applied in industry, since it is easy to prepare and conduct and results can be obtained quickly and cheaply. A disadvantage is that some results are only comparative.[1]

The test was developed around 1900 by S. B. Russell (1898, American) and G. Charpy (1901, French). [2] The test became known as the Charpy test in the early 1900s due to the technical contributions and standardization efforts by

  • Video on the Charpy impact test
  • Charpy Impact Testing module at steeluniversity.org, including a fully interactive simulation
  • Online Curvefitting Calculator for Charpy Impact Testing

External links

  1. ^ a b c Meyers Marc A, Chawla Krishan Kumar (1998). Mechanical Behaviors of Materials. Prentice Hall.  
  2. ^ Siewert
  3. ^ a b c The Design and Methods of Construction of Welded Steel Merchant Vessels: Final Report of a (U.S. Navy) Board of Investigation (July 1947). "Welding Journal" 26 (7,). Welding Journal. p. 569. 
  4. ^ Williams, M. L. and Ellinger, G. A (1948). Investigation of Fractured Steel Plates Removed from Welded Ships. National Bureau of Standards Rep. 
  5. ^ Siewert, T. A., Manahan, M. P., McCowan, C. N., Holt, J. M., Marsh, F. J., and Ruth, E. A (1999). Pendulum Impact Testing: A Century of Progress, ASTM STP 1380. ASTM. 
  6. ^ Cedric W. Richards (1968). Engineering materials science. Wadsworth Publishing Company, Inc. 
  7. ^ Kurishita H, Kayano H, Narui M, Yamazaki M, Kano Y, Shibahara I (1993). "Effects of V-notch dimensions on Charpy impact test results for differently sized miniature specimens of ferritic steel". Materials Transactions - JIM (Japan Institute of Metals) 34 (11): 1042–52.  
  8. ^ Mills NJ (February 1976). "The mechanism of brittle fracture in notched impact tests on polycarbonate".  
  9. ^ ASTM E23 Standard Test Methods for Notched Bar Impact Testing of Metallic Materials
  10. ^ a b ISO 148-1 Metallic materials - Charpy pendulum impact test - Part 1: Test method
  11. ^ a b EN 10045-1 Charpy impact test on metallic materials. Test method (V- and U-notches)
  12. ^ Mathurt KK, Needleman A, Tvergaard V (May 1994). "3D analysis of failure modes in the Charpy impact test". Modeling and Simulation in Materials Science Engineering 2 (3A): 617–35.  
  13. ^ ASTM A370 Standard Test Methods and Definitions for Mechanical Testing of Steel Products

Notes

See also

According to ISO 148,[10] standard specimen sizes are 10 mm × 10 mm × 55 mm. Subsize specimens are: 10 mm × 7.5 mm × 55 mm, 10 mm × 5 mm × 55 mm and 10 mm × 2.5 mm × 55mm.

According to EN 10045-1,[11] standard specimen sizes are 10 mm × 10 mm × 55 mm. Subsize specimens are: 10 mm × 7.5 mm × 55 mm and 10 mm × 5 mm × 55 mm.

According to ASTM A370,[13] the standard specimen size for Charpy impact testing is 10 mm × 10mm × 55mm. Subsize specimen sizes are: 10 mm × 7.5 mm × 55mm, 10 mm × 6.7 mm × 55 mm, 10 mm × 5 mm × 55 mm, 10 mm × 3.3 mm × 55 mm, 10 mm × 2.5 mm × 55 mm. Details of specimens as per ASTM A370 (Standard Test Method and Definitions for Mechanical Testing of Steel Products).

Sample sizes

The qualitative results of the impact test can be used to determine the ductility of a material.[12] If the material breaks on a flat plane, the fracture was brittle, and if the material breaks with jagged edges or shear lips, then the fracture was ductile. Usually a material does not break in just one way or the other, and thus comparing the jagged to flat surface areas of the fracture will give an estimate of the percentage of ductile and brittle fracture.[1]

Qualitative results

The ductile-brittle transition temperature (DBTT) may be derived from the temperature where the energy needed to fracture the material drastically changes. However, in practice there is no sharp transition and it is difficult to obtain a precise transition temperature (it is really a transition region). An exact DBTT may be empirically derived in many ways: a specific absorbed energy, change in aspect of fracture (such as 50% of the area is cleavage), etc.[1]

The quantitative result of the impact tests the energy needed to fracture a material and can be used to measure the toughness of the material. There is a connection to the yield strength but it cannot be expressed by a standard formula. Also, the strain rate may be studied and analyzed for its effect on fracture.

Quantitative results

The "Standard methods for Notched Bar Impact Testing of Metallic Materials" can be found in ASTM E23,[9] ISO 148-1[10] or EN 10045-1,[11] where all the aspects of the test and equipment used are described in detail.

The notch in the sample affects the results of the impact test,[7] thus it is necessary for the notch to be of regular dimensions and geometry. The size of the sample can also affect results, since the dimensions determine whether or not the material is in plane strain. This difference can greatly affect conclusions made.[8]

The apparatus consists of a pendulum of known mass and length that is dropped from a known height to impact a notched specimen of material. The energy transferred to the material can be inferred by comparing the difference in the height of the hammer before and after the fracture (energy absorbed by the fracture event).

A vintage impact test machine.

Definition

[6] In 1896 S. B. Russell introduced the idea of residual fracture energy and devised a pendulum fracture test. Russell's initial tests measured un-notched samples. In 1897 Frémont introduced a test trying to measure the same phenomenon using a spring-loaded machine. In 1901

History

Contents

  • History 1
  • Definition 2
  • Quantitative results 3
  • Qualitative results 4
  • Sample sizes 5
  • See also 6
  • Notes 7
  • External links 8

Today it is utilized in many industries for testing materials, for example the construction of pressure vessels and bridges to determine how storms will affect the materials used.[3][3][5]

[4][3]

This article was sourced from Creative Commons Attribution-ShareAlike License; additional terms may apply. World Heritage Encyclopedia content is assembled from numerous content providers, Open Access Publishing, and in compliance with The Fair Access to Science and Technology Research Act (FASTR), Wikimedia Foundation, Inc., Public Library of Science, The Encyclopedia of Life, Open Book Publishers (OBP), PubMed, U.S. National Library of Medicine, National Center for Biotechnology Information, U.S. National Library of Medicine, National Institutes of Health (NIH), U.S. Department of Health & Human Services, and USA.gov, which sources content from all federal, state, local, tribal, and territorial government publication portals (.gov, .mil, .edu). Funding for USA.gov and content contributors is made possible from the U.S. Congress, E-Government Act of 2002.
 
Crowd sourced content that is contributed to World Heritage Encyclopedia is peer reviewed and edited by our editorial staff to ensure quality scholarly research articles.
 
By using this site, you agree to the Terms of Use and Privacy Policy. World Heritage Encyclopedia™ is a registered trademark of the World Public Library Association, a non-profit organization.
 



Copyright © World Library Foundation. All rights reserved. eBooks from World eBook Library are sponsored by the World Library Foundation,
a 501c(4) Member's Support Non-Profit Organization, and is NOT affiliated with any governmental agency or department.